Product Features:
WeiKeLai (WKL) Chromium Carbide Overlay Plate consists of a mild
steel base plate onto which a highly abrasive resistant welded overlay deposited
with Open Arc Welding. The overlay deposit is either one or two layers.
Transverse cracks occur on the surface as a natural phenomenon
during welding due to stress release, which under control by the chemical
composition of the overlay or by cooling methods. The cracks have no any effections
on the performance of wear plate.
Compound wear plate has its unique metallographic
structure and hardness can reach to HRc 56~HRc62 which could make sure
excellent wear property. Meanwhile, it is also of good machinability and
available to cut, bending, welding and other processing with recommended
method.
WKL wear plate has high content of chromium with
overlay, and other chemical components like Manganese, Molybdenum, Niobium, Vanadium,
etc鈥 are also contained for various applications requested.
脴 Flat & smooth surface
脴 Outstanding wear resistant property
脴 Economical production cost
脴 Available to form wear part in various shape
脴 Moderate impact resistance & Good temperature resistance
脴 Good weldability to most structural steel
Plate Spec
|
Base plate (mm)
|
Overlay (mm锛
|
Hardness锛HRc锛
|
Standard Size(L*W )/mm
|
WA10mm(6+4)
|
6
|
4
|
54-58
|
A. 2,000*1,200
B. 1,500*3,000
C. Both thickness & Size
are available to meet customer鈥檚 request
|
WA12mm(6+6)
|
6
|
6
|
56-60
|
WA14mm(8+6)
|
8
|
6
|
56-60
|
WA18mm(10+8)
|
10
|
8
|
56-62
|
WA16mm(12+4)
|
12
|
4
|
54-58
|
|